Threaded joint for an oil well pipe

ABSTRACT

Oil well pipe component comprising a threaded portion, at least part whereof is coated with a layer of a corrosion-inhibiting material, that has been applied to at least the part of the threaded portion of the oil well pipe component by means of a method comprising a cataphoresis step from an aqueous bath, said method comprising—providing the oil well pipe component comprising a threaded portion; —immersing at least part of the threaded portion of the pipe component in a cataphoresis bath comprising water and suspended particles of corrosion-inhibiting material, and provided with an anode and a cathode means, the pipe component being connected to the cathode means; —inducing a current through the bath, in order to provide the corrosion-inhibiting material with a positive charge; —depositing a layer of the positively charged corrosion-inhibiting material onto the pipe component; and—removing the immersed part of the pipe component with the layer of corrosion-inhibiting material from the cataphoresis bath and allowing the corrosion-inhibiting material to set.

The present invention relates to an oil well pipe component comprising a threaded portion that is coated with at least a layer of a corrosion-inhibiting material. The invention further relates to a method for applying a layer of a corrosion inhibiting material to the oil well pipe component.

Pipes and components thereof often require a coating that prevents the pipe or the component in question from corrosion. That particularly applies to threaded pipes that are used in the oil and gas industry. In this industry pipe segments having threaded portions can be joint to form a pipeline or pipe string. The pipe segments may for example be joined by means of connectors that have internal threaded portions and mate with the external threaded portions of the pipe segments. In other embodiments, an external threaded portion of a pipe segment is connected with an internal threaded portion of another pipe segment. The pipe segments with one or more external threaded portions are often referred to as the male component of the joint, or as pin members. The internal threaded portions in the pipe segments or in the connectors are referred to as the female components of the joint or as box members.

As described in US 2004/0113423, in the oil fields it is common practice to use metallic pipes of a predefined length, joined to form such a string to reach the depth in which there are oil or gas reservoirs or pools for their extraction. This extraction technique requires to gradually case the well internally, during its boring, which is performed with metallic tubes, the so-called casing of the well. Once the desired depth is reached, there is placed a string of metallic pipes of smaller diameter, the so-called tubing, to pump the gaseous or liquid hydrocarbons to the surface. Both casing and tubing strings are formed of pipe segments, which are joined together using threaded connectors.

It is evident that the use of these tubing and casing strings are subjected to a harsh environment where corrosion and galling may easily occur. By corrosion is understood the gradual destruction of the metals in the steel object by chemical reactions with its environment. Usually this refers to the degradation of the steel object due to the reaction with an oxidant, such as oxygen itself. By galling is meant the formation of surface damage that arises between sliding surfaces having metal-to-metal contact. Galling may be caused by unevenness of the sliding surfaces.

For these reasons it is customary to coat the tubing and casing strings, and in particular the threaded portions of these strings with a protective coating to render the strings better resistant to corrosion and galling. In the above-mentioned US 2004/0113423 it has been described that the threaded portion of a pipe segment having external threads has been coated with a first layer of a corrosion-inhibiting material and a second layer of a lubricant coating. It is observed that the female component of the joint, having internal threads, may be left without protective layers and be connected to a male component with the protective layer.

Although this may be a satisfactory solution, when the male and female components have been mated, it leaves the female component unprotected during transport and storage. To overcome this problem US 2004/0113423 also discloses the possibility to coat both the male and the female components. As examples of methods to apply the layers reference is made to spraying, dipping and brushing.

As an alternative solution, it is proposed in US 2012/0112456 to apply a photocurable coating to at least one of the threaded portions of a pin and a box, and cure the composition. Also these coatings are applied onto the substrate by spraying, showering, dipping, or by roll application.

A drawback of these methods for applying a layer of protective coating resides in that the uniformity of the layer thickness cannot be guaranteed. As indicated above, galling can be caused by unevenness of the sliding parts. When the surface of threaded portion of a male or female member is not sufficiently even, galling may arise. In addition, when the coatings are not uniform, fluctuations in torque may occur. The sealing mechanisms of commonly used types of threaded tubular connections is discussed in a Journal of Petroleum Technology article, March 1967, page 337, “New Technology For Improved Tubular Connection Performance”, by P. D. Weiner and F. D. Sewell. The authors indicate inter alia that connection make-up torque depends primarily on the friction between the mating pin and box threads which, for clean connections, is largely a function of the type of thread compound employed. The authors show that employing different types of thread compounds can cause connection make-up torque variations of up to 500 percent. It is evident that when the coatings of the connection is non uniform the friction may increase and thus the torque may fluctuate.

In U.S. Pat. No. 5,645,890 reference is made to a study wherein the intrinsically conductive polymer polyaniline is deposited electrochemically on stainless steel. It is, however, observed that these coatings are not applicable for the prevention of corrosion of most metal structures. Therefore, U.S. Pat. No. 5,645,890 discloses the prevention of corrosion on metal objects by using a polyaniline coating that has been applied by spraying a polyaniline solution, brushing such a solution or immersing the metal surface in such a solution. The polyaniline has been dissolved in an organic solvent such as dimethylsulphoxide, N-methyl pyrrolidone (NMP), and tetramethyl urea.

Polyaniline has also been considered for use as corrosion-inhibiting material in tubing and casing strings, as disclosed in US 2005/0176592. This application aims at protecting the internal threading of a female component of a joint with polyaniline and a lubricant whilst the male component of the joint may be coated with polyaniline only. According to the disclosure of US 2005/0176592 the polyaniline may be deposited onto the threaded portion of the box and pin by means of spraying, brushing, electrophoresis and electropolymerization of the monomer or monomers. In order to apply the polyaniline, the polyaniline is taken up in a solution with NMP. In an example the solution of polyaniline in NMP is sprayed over the metal surface to be treated.

A drawback of the known process is that the method requires large amounts of volatile organic solvents. The evaporation thereof is environmentally unfriendly. Further, it is evident that this application fails to recognize that the evenness of the layer of corrosion-inhibiting material can be improved if spraying is replaced by an electrochemical deposition method. Moreover, as is known from Bull. Chem. Soc. Jpn, 57, 2254-2257, (1984) polyaniline can be anodically deposited onto an anode electrode.

In order to overcome the drawbacks of the prior art it has now been found that when cataphoresis from an aqueous bath is used in the deposition of corrosion-inhibiting material onto an oil well pipe component, a layer with a uniform thickness is obtained. Moreover, since water is the main liquid diluent for the corrosion-inhibiting material, the process for preparing the layer by cataphoresis does not incur a significant evaporation of organic vapors.

Accordingly, the present invention provides an oil well pipe component comprising a threaded portion that is a sleeve-shaped coupling member for a cylindrical oil well pipe, comprising an internal threaded portion, or a cylindrical oil well pipe comprising an external threaded portion, wherein at least part of the threaded portion is coated with a layer of a corrosion-inhibiting material, that has been applied to at least the part of the threaded portion of the oil well pipe component by means of cataphoresis from an aqueous bath.

The invention also provides a method for coating an oil well pipe component comprising a threaded portion with a layer of a corrosion-inhibiting material, comprising

-   -   providing an oil well pipe component comprising a threaded         portion, which is a sleeve-shaped coupling member for a         cylindrical oil well pipe, comprising an internal threaded         portion, or a cylindrical oil well pipe comprising an external         threaded portion;     -   immersing at least part of the threaded portion of the pipe         component in a cataphoresis bath comprising water and suspended         particles of corrosion-inhibiting material, and provided with an         anode and a cathode means, the pipe component being connected to         the cathode means;     -   inducing a current through the bath, in order to provide the         corrosion-inhibiting material with a positive charge;     -   depositing a layer of the positively charged         corrosion-inhibiting material onto the pipe component; and     -   removing the immersed part of the pipe component with the layer         of corrosion-inhibiting material from the cataphoresis bath and         allowing the corrosion-inhibiting material to set.

It is understood that the oil well pipe component according to the invention includes pipe components that are suitable for oil well applications. That implies that also the pipe components according to the invention may also be used in other field applications, such as the exploration and production of gas.

The present invention allows the provision of an oil well pipe component, made from steel or alloys, such as a pin member or a box member that has been prepared in an environmentally friendly way and with a thin layer of corrosion-inhibiting material which layer has a uniform thickness. This represents a considerable advantage over the prior art documents mentioned that employ a different way of application. Also US 2005/0176592, which mentions electrophoresis, suggesting anodic deposition, and also indicates that polyaniline is to be deposited from an organic solution, fails to suggest the present invention. From U.S. Pat. No. 5,976,337 it is known that electrophoretic depositions may be conducted in a bath comprising organic solvents with low viscosity and low surface tension, including nitrogen-containing solvents. Hence, none of these documents mentioned above teaches or suggests that the provision of a coating of a corrosion-inhibiting layer by means of cataphoresis from a water-containing bath would lead to a uniform thickness of such layer. A box member and pin member may also comprise unthreaded portions. These unthreaded portions comprise for instance torque shoulders and metal-to-metal sealing surfaces in oil well pipe components. When the oil well pipe component is being subjected to cataphoresis such unthreaded portions are also advantageously coated with corrosion-inhibiting material in an even way. Since the coatings on also the metal-to-metal sealing surfaces comprise a coating with an even thickness, the sealing action is facilitated.

Here it is noted that electrophoretic deposition of a corrosion-inhibiting coating on small objects, such as bolts and nuts for use in industry, automotive and aerospace is known per se, e.g. from WO 2006/020857, GB 2008618, U.S. Pat. No. 5,753,316 and U.S. Pat. No. 5,385,655. In these technical fields such small objects do not encounter problems relating to galling, lubricating and torque fluctuations as occur in land and marine oil fields, in particular during the make-up of the operation.

Typically the oil well pipe component according to the invention belongs to the so called Oil Country Tubular Goods (OCTG), which satisfy API Specification 5CT. OCTG like tubing and casing are used in the excavation of oil wells for exploration of oil and gas fields. At present, deep oil wells e.g. in offshore oil fields may reach up to a depth of 10 000 meters. Typically the well pipes having a defined length of several tens of meters are mutually connected by threaded joints using a sleeve-shaped coupling member. Airtightness of the threaded joints is mandatory. Upon use the threaded joints for connecting OCTG are exposed to axial tensile forces that are caused by the weight of the OCTG and the threaded joints. Furthermore, the internal and external pressure are important parameters. Even under these harsh conditions prevailing in oil and gas fields the threaded joints need to maintain airtightness.

Typically the threaded joint for OCTG comprises a pin-box structure. A pin member is a male threaded end portion of an oil well pipe. A box member is a female threaded portion on the inner surface of the sleeve-shaped coupling member. Usually an unthreaded contact section is present at the end of the male thread of the pin. A matching unthreaded metal contact section is also present at the base of the female thread in the sleeve-shaped coupling member. Moreover, the sleeve-shaped coupling member may comprise a contact shoulder. Upon inserting the pin member into the box member and fastening the threads thereof to one another, the unthreaded contact sections will contact each other, thereby forming a metal-to-metal seal. This seal ensures the required airtightness.

In the oil well pipe component the threaded portion thereof is at least partly coated with a layer of a corrosion-inhibiting material. The corrosion-inhibiting material can be selected from known corrosion-inhibiting materials. It is evident that for the present invention the corrosion-inhibiting material must be capable of being deposited onto a pipe element in a cataphoresis process. Such materials are well-known in the art. In particular in the art of the production of bodies for automobiles many corrosion-inhibiting materials are known. Suitably the corrosion-inhibiting material comprises a resin that is responsive to an electric field. Typically, the resin is selected from the group consisting of polyolefins, saturated and unsaturated polyesters, alkyd resins, acrylic resins, phenolic resins, polyamides, epoxy resins and polyurethane resins. It has been found that very good results are obtainable when the corrosion-inhibiting material comprises a basic resin. In particular amino epoxy resins and amino-urethane resins and combinations thereof yield very good results. Many such corrosion-inhibiting materials are commercially available. Examples of base resins that can be used in cataphoresis baths are described in a large number of patent documents, including EP-A-082 291, EP-A-234 395, EP-A-209 857, EP-A-227 975, EP-A-178 531, EP-A-333 327, EP-A-310 971, EP-A-456 270, U.S. Pat. No. 3,922,253, EP-A-261 385, EP-A-245 786, DE-33 24 211, EP-A-414 199 and EP-A-476 514. The resins described therein can be used alone or in a mixture.

Good results have been obtained with corrosion-inhibiting materials comprising epoxy resins, polyamides, polyurethanes and combinations thereof. An example of a commercially available material is Cathoguard®, available from BASF, being an aqueous emulsion of an epoxy resin with an isocyanate cross-linker. Other examples include Aqua EC 3000 from Herberts and Enviroprime® from PPG.

As indicated above, the pipe elements according to the invention have a very uniform layer of corrosion-inhibiting material. Suitably, the thickness of the layer is in the range of 10 to 30 μm. It is evident that when the thickness of the layer is relatively thin, the aspect of uniformity becomes very important. Although variances in thickness may in absolute terms be relatively small, such variances may be proportionally large and have serious consequences as to the prevention of galling and corrosion. Therefore, thanks to the application via an aqueous cataphoresis bath, the pipe elements according to the present invention have a layer of corrosion-inhibiting material with a uniform thickness, i.e. a thickness does have a variance in thickness of not more than 20 μm. Advantageously, the variance in thickness is at most 6 μm. These degrees of uniformity can be achieved by the cataphoretic application of the corrosion-inhibiting material. Expressed in the format of a standard deviation, the thickness has a standard deviation that is suitably at most 5 μm, more preferably at most 3 μm.

It is known in the art to improve the adherence of resins to oil well pipe components by means of a layer of one or more phosphates. Therefore, the pipe component according to the invention preferably comprises further at least partly a phosphate layer between the layer of corrosion-inhibiting material and the threaded portion of the pipe component. The phosphate layer suitably comprises one or more compounds selected from zinc phosphate, manganese phosphate, nickel phosphate and iron phosphate. Methods for applying such a phosphate layer are known in the art. In that respect reference is made to application WO 2012/010981 wherein such a phosphate layer is applied to the male threaded portions of a pipe element. The thickness of the phosphate layer may typically range from 2 to 20 μm, preferably from 4 to 10 μm. In U.S. Pat. No. 4,233,088 a method is described for inhibiting corrosion and providing a foundation for subsequent application of a coating system to steel surfaces, which method comprises the development of a protective phosphatizing reaction coating based on a metal other than the metal which is to be protected either by an immersion treatment or by a spray treatment with a phosphatizing bath which contains the metal phosphate or metal acid phosphate matter for such a treatment in a status nascendi. Such a state is obtained by the use of an aqueous medium containing phosphate ions derived from an alkali metal phosphate, an alkali metal acid phosphate, phosphoric acid or combinations of those and introducing into the aqueous medium a metal oxide based on a metal other than that which is to be treated, preferably an oxide of the metal group of molybdenum, vanadium, tungsten, titanium, lead, manganese and copper, whereby the metal oxide in the aqueous medium forms with the phosphate ions of the aqueous medium the desired freshly prepared metal phosphate or metal acid phosphate to develop on the treated metal surface the required protective reaction coating. The phosphatizing bath can be modified further by introducing into the aqueous medium a ligand-forming organic polymer which is capable of entering the reaction coating formation and said polymer can further be influenced also by the addition into the aqueous medium of a small amount of an acetylenic alcohol or a dialdehyde. Also a dispersing agent, such as formamide or an alkyl-substituted formamide, can be employed to increase the reactivity of the metal oxide component.

The layer of corrosion-inhibiting material may comprise additional components in addition to the resin that is deposited in the cataphoretic bath. Such additional components may be selected from additional anti-corrosion compounds. Such compounds include e.g. nitrogen-containing compounds and dithiophosphates. It is also possible to select specific resins that have excellent anti-corrosion properties.

It is also feasible to ensure that the layer of corrosion-inhibiting material further comprises a lubricant, preferably particles of a solid lubricant. Preferably, the layer of corrosion-inhibiting material is covered by an additional layer comprising a lubricant, in particular a dry lubricant, preferably particles of a solid lubricant. Due to the lubricant in or onto the layer, the fastening of the pipe components becomes less difficult and galling is reduced or even prevented. The lubricants that can be used in these applications are generally known in the art. Suitable examples of such solid lubricants are molybdenum disulfide, tungsten disulfide, boron nitride, graphite, polytetrafluoroethylene (PTFE), and combinations thereof.

The oil well pipe components suitable for the present invention, include so-called pin members and box members of pipelines used for the drilling and/or production of oil fields. The pipe component according to the present invention is at least one of a sleeve-shaped coupling member for a cylindrical oil well pipe, comprising an internal threaded portion, or a cylindrical oil well pipe comprising an external threaded portion, or both. Persons skilled in the art will realize that it is more feasible to subject a box member to a cataphoresis process than a pin member, just for reasons of size. Therefore, the pipe component is preferably a box member, i.e. a sleeve-shaped coupling member for a cylindrical oil well pipe. Typically such a sleeve-shaped coupling member is provided with internal threaded portions at both ends of the sleeve, which portions are separated from one another by an unthreaded portion. The unthreaded portion may comprise a metal to metal contact section (disposed substantially axially with respect to the axis of the connection) in order to form an airtight seal upon assembling; also the unthreaded portion may comprise an abutment shoulder (disposed substantially radially with respect to the axis of the connection).

The invention also provides an assembly (i.e. a string) of at least two oil well pipes, which are mutually connected by means of a sleeve-shaped coupling member, wherein at least one the assembling parts, preferably including the coupling member, is an oil well component according to the invention. Such an assembly having a threaded joint profits from the advantageous corrosion-inhibiting and galling-reducing properties of the coating that is applied by cataphoresis.

As indicated above, the invention also provides a method for coating an oil well pipe component. An essential step in this method is the application of a corrosion-inhibiting material on the oil well pipe component by means of a cataphoresis in an aqueous bath. The operation of a cataphoresis bath is known in the art. In a cataphoresis process, also known as cathodic electrodeposition, positively charged particles in an electric field are moved toward an oppositely charged metallic surface. In this way the surface is provided with a layer of the particles. This process enables the deposition of a layer of material on surfaces that may be difficult to reach. In addition, it has been found that the process also enables the provision of a layer of uniform thickness. The cataphoresis process may be carried out in a known manner applying a voltage of 50 to 500 V, preferably from 100 to 350 V. The current density suitably ranges from 0.1 to 40 A/m². As indicated above, the corrosion-inhibiting material suitably comprises a resin that is responsive to an electric field. Typically, the resin is selected from the group consisting of polyolefins, saturated and unsaturated polyesters, alkyd resins, acrylic resins, phenolic resins, epoxy resins and polyurethane resins. It has been found that very good results are obtainable when the corrosion-inhibiting material comprises a basic resin. In particular amino epoxy resins and amino-urethane resins yield very good results. The cataphoretic bath suitably comprises from 55 to 95% wt of water, preferably from 70 to 90% wt of water and 45 to 5% wt, preferably from 30 to 10% wt of corrosion-inhibiting material. The duration of the cathodic deposition may vary in dependence of the desired thickness of the coating, and the voltage and current density applied. Typically, the duration of the cathodic deposition is in the range of 1 to 10 minutes, preferably from 2 to 8 minutes.

Before the surface of the oil well pipe component is being subjected to cathodic electrodeposition, the oil well pipe component may suitably be subjected to a pre-treatment before it is immersed into the cataphoresis bath. Advantageous pre-treatments include degreasing, washing and phosphatisation and combinations thereof. It is also advantageous to subject the surface of the oil well pipe component to a mechanical pre-treatment, in particular an abrasive blasting step. In such a step the surface of the oil well pipe component is roughened by blasting the oil well pipe component with abrasive material, such as sand, glass, alumina, corundum or combinations thereof. The surface thus treated may provide an improved adhesion for the subsequent coating or coatings. Such a subsequent coating is preferably provided by a layer of a phosphate, as described hereinbefore. Thereto, the oil well pipe component, optionally after an abrasive blasting step, is subjected to phosphatizing by spraying with or dipping in a composition comprising zinc phosphate, manganese phosphate, nickel phosphate and/or iron phosphate.

Galling of the threads in oil well pipe components may be reduced or prevented by using a lubricant. Therefore, it is advantageous if the layer on top of the threaded portions of the oil well pipe component also comprises a lubricant. It is advantageous to use suspended particles of corrosion-inhibiting material in the cataphoresis bath which particles further comprise a solid lubricant. In this way the lubricant is evenly spread over the surface of the threaded portion of the pipe component. At the same time it is ensured that the uniformity of the thickness of the layer is not affected. The lubricant that can be used in these applications are generally known in the art. Suitable examples of such solid lubricants are molybdenum disulfide, tungsten disulfide, boron nitride, graphite, polytetrafluoroethylene (PTFE), and combinations thereof. Preferably a lubricant is applied separate from the corrosion-inhibiting material, or if a lubricant is desired in addition to the solid lubricant that is contained in the corrosion-inhibiting material, the pipe component, after having allowed the corrosion-inhibiting material to set, may be at least partly covered, in particular the threaded portion, with a layer of lubricant. In case of a solid lubricant the lubricant may be the same as those mentioned hereinbefore. In such cases the solid lubricant may be comprised in a matrix such as a resin or binder material. Alternatively, a viscous liquid lubricant may be applied. A dry solid lubricant top layer is a preferred embodiment.

When the oil well pipe component, such as a box member for a casing, has been coated with a layer of corrosion-inhibiting material and is taken out of the cataphoresis bath in which it was immersed, the corrosion-inhibiting material is typically allowed to set. The setting of the material, also known as curing, can be done in any known manner. Suitably, the setting is performed by treating the pipe component to a treatment of maintaining at least the threaded portion of the pipe component to an elevated temperature. Suitable temperatures are in the range of 50 to 250° C. This elevated temperature is suitable maintained for a period in the range of 1 to 120 minutes, preferably from 5 to 60 minutes. In this manner the layer of corrosion-inhibiting material is firmly fixed to the surface of the pipe component and at the same time it forms a solid smooth seal layer that prevents water, oxygen and other contaminants from contacting the metallic surface of the pipe component. Excellent results are obtained at a temperature of about 160 to 170° C. for about 30 to 50 minutes.

In accordance with the invention several preferred embodiments can be prepared. A first embodiment comprises a layer of corrosion-inhibiting material that has been deposited by cataphoresis on the surface of an oil well pipe component, for example the box member of a casing or pipeline, which surface may optionally having been subjected to abrasive blasting and/or to the deposition of a phosphate layer. In a second embodiment the layer of corrosion-inhibiting material may further comprise a solid lubricant. Also in this case the surface of the pipe component may have been treated by abrasive blasting and/or phosphatizing. In a third embodiment, the layer of corrosion-inhibiting material, optionally comprising a solid lubricant, and optionally deposited on a surface that has been treated with abrasive blasting and/or phosphatizing, is coated with a layer of a lubricant, which may be a solid, or a solid contained in a matrix, or a liquid, suitably a viscous liquid. The skilled person will realize that other embodiments are also contained in the description of the present invention.

The invention is elucidated by means of the following Figures, wherein

FIG. 1 schematically shows a threaded portion according to the prior art and

FIG. 2 shows such a threaded portion according to the invention.

FIG. 1 shows a cross-sectional view of a portion of a wall of an oil well pipe component 1 along the axis of the pipe component, to which a layer 2 of a corrosion-inhibiting material has been applied by means of spraying. It is shown how the layer 2 of the corrosion-inhibiting material has a varying thickness along the threaded portion. In particular, the flanks of the threads tend to have a thinner coating that the roots or the crests.

In FIG. 2 a similar oil well pipe component 3 is shown whereon a layer of corrosion-inhibiting material 4 has been deposited via cataphoresis. It is shown how the thickness of the layer of corrosion-inhibiting material is uniform along the entire threaded portion. The Figures show the difference in uniformity of the layer thickness, in particular on the flanks of the threaded portions.

The invention will be further elucidated by means of the following Examples.

EXAMPLE 1

A steel box member that is used as an oil well pipe component was in a known way degreased and washed and then phosphatized with manganese phosphate. Then the box member was immersed in a cataphoresis bath containing a commercial cataphoretic paint Cathoguard®325 and subjected to cataphoretic deposition for about 3 minutes at a voltage of 250-380V. The coating was cured for about 50 minutes at 160° C. Subsequently, a layer of solid lubricant, comprising polytetrafluoroethylene was applied on the layer of corrosion-inhibiting material by spraying the inner threaded portion of the box member by means of a turbine producing a radial spray coating.

Via SEM (scanning electron microscopy) the thickness of the coatings on the threads was determined on the roots, the flanks and the crests of the threaded portion of the box member. The thickness was determined for both the layer of corrosion-inhibiting material and the solid lubricant. The results are shown in the Table 1 below, wherein the values represent the average of various measurements. The variation between the individual values of the thickness of the corrosion-inhibiting material on the flanks was about 4.5 μm, there was virtually no variance on the crest, and the variance on the root was about 0.3 μm.

TABLE 1 Thickness Thickness corrosion-inhibiting layer, μm solid lubricant, μm Flanks 23.2 17.3 Crest 23.7 29.7 Root 20.6 9.00

From the results it is clear that the thickness of the layer of corrosion-inhibiting material applied by cataphoresis is much more uniform than the layer of solid lubricant that is applied via spraying.

Comparative Example 1

For comparison reasons an oil well pipe component comprising a threaded portion was pretreated and phosphatized in the manner described in Example 1. The thus treated oil well pipe component was further coated with an epoxy-based corrosion-inhibiting coating according to the teachings of US 2008/129044 by means of spraying, which coating composition also comprised polytetrafluoroethylene as solid lubricant. The thickness of the corrosion-inhibiting coating was determined and the results of the average values are shown in Table 2.

TABLE 2 Thickness corrosion-inhibiting layer, μm Flanks 19.9 Crest 84.0 Root 37.3

It was found that the thickness on the flanks, the crest and the root was not very uniform. Moreover, it was found that the variance of the coating on the flanks was about 6 μm, the variance on the crest was about 12 μm, and the variance on the root was about 3 μm.

Example 2

The box member of Example 1 was placed in a salt spray chamber and subjected to salt spray tests for 1500 hours in accordance with ASTM B-177. The assessment of the degree of corrosion was determined in accordance with grades of ASTM D-610. According to this ASTM standard, the degree of corrosion is rated from 1 to 10, wherein the various grades represent certain percentages of corroded area, as indicated in Table 3 below.

TABLE 3 grade 10 9 8 7 6 5 4 3 2 1 Area, % 0-0.03 0.03-0.1 0.1-0.3 0.3-1 1-3 3-10 10-16 16-33 33-50 50-100

Additional qualifications are given in accordance with the following scale:

S (spot) Corrosion localized in small areas G (general) Corrosion distributed randomly P (pinpoint) Corrosion present as little dispersed points H (hybrid) Corrosion can be a combination of any of the above cases

The threaded portion of one particular specimen showed the following corrosion after subjection to the salt spray tests for the duration as specified in Table 4.

For comparison purposes the box member of Comparative Example 1 was also subjected to this test. The results are also shown in Table 4.

TABLE 4 Corrosion grade, Corrosion grade, Duration, hrs Example 1 Comp. Example 1 48 9P 9P 168 9P 8G 336 9P 7G 504 9P 6G 552 9P 5P 960 9P n.d. 1224 8P n.d. 1512 7P n.d. n.d. = not determined

These results show that the threaded portion as protected by the layer of corrosion-inhibiting material and solid lubricant shows an excellent corrosion behavior. The results further show that the non-uniformity of the layers in the comparative example leads to more severe corrosion, despite the fact that the corrosion-inhibiting layer has a bigger thickness than the layer in Example 1. 

1. Oil well pipe component comprising a threaded portion, being a sleeve-shaped coupling member for a cylindrical oil well pipe, comprising an internal threaded portion, or a cylindrical oil well pipe comprising an external threaded portion, wherein at least part of the threaded portion is coated with a layer of a corrosion-inhibiting material, that has been applied to at least the part of the threaded portion of the oil well pipe component by means of cataphoresis from an aqueous bath.
 2. Pipe component according to claim 1, which is a sleeve-shaped coupling member for a cylindrical oil well pipe.
 3. Pipe component according to claim 2, wherein the sleeve-shaped coupling member is provided with internal threaded portions at both ends of the sleeve, which portions are separated from one another by an unthreaded portion.
 4. Pipe component according to any one of the preceding claims, wherein the layer of corrosion-inhibiting material is covered by an additional layer comprising a lubricant.
 5. Pipe component according to any one of the preceding claims 1-3, wherein the layer of corrosion-inhibiting material further comprises a lubricant.
 6. Pipe component according to claim 4 or 5, wherein the lubricant comprises particles of a solid lubricant.
 7. Pipe component according to any one of claims 4 to 6, wherein the lubricant has been selected from molybdenum disulfide, tungsten disulfide, boron nitride, graphite, polytetrafluoroethylene (PTFE), and combinations thereof.
 8. Pipe component according to any one of the preceding claims, wherein the corrosion-inhibiting material comprises a resin.
 9. Pipe component according to any one of the preceding claims, wherein the corrosion-inhibiting material is selected from the group consisting of amino epoxy resins, amino-urethane resins and combinations thereof.
 10. Pipe component according to any one of the preceding claims, wherein the corrosion-inhibiting material comprises one or more of the resins selected from the group consisting of polyolefins, saturated and unsaturated polyesters, alkyd resins, acrylic resins, phenolic resins, polyamides, epoxy resins and polyurethane resins.
 11. Pipe component according to any one of the preceding claims, wherein the thickness of the layer of corrosion-inhibiting material is in the range of 10 to 30 μm.
 12. Pipe component according to any one of the preceding claims, which further at least partly comprises a phosphate layer between the layer of corrosion-inhibiting material and the threaded portion of the pipe component,
 13. Pipe component according to claim 12, wherein the phosphate layer comprises one or more compounds selected from zinc phosphate, manganese phosphate, nickel phosphate and iron phosphate.
 14. Method for coating an oil well pipe component comprising a threaded portion with a layer of a corrosion-inhibiting material, comprising providing a pipe component comprising a threaded portion being a sleeve-shaped coupling member for a cylindrical oil well pipe, comprising an internal threaded portion, or a cylindrical oil well pipe comprising an external threaded portion; immersing at least part of the threaded portion of the pipe component in a cataphoresis bath comprising water and suspended particles of corrosion-inhibiting material, and provided with an anode and a cathode means, the pipe component being connected to the cathode means; inducing a current through the bath, in order to provide the corrosion-inhibiting material with a positive charge; depositing a layer of the positively charged corrosion-inhibiting material onto the pipe component; and removing the immersed part of the pipe component with the layer of corrosion-inhibiting material from the cataphoresis bath and allowing the corrosion-inhibiting material to set.
 15. Method according to claim 14, wherein the oil well pipe component comprising a threaded portion is a sleeve-shaped coupling member for a cylindrical oil well pipe.
 16. Method according to claim 14 or 15, wherein the corrosion-inhibiting material comprises a resin, preferably selected from amino epoxy resins, amino-urethane resins and combinations thereof.
 17. Method according to any one of the claims 14 to 16, wherein the pipe component has been subjected to a pre-treatment before being immersed into the cataphoresis bath, preferably at least one pre-treatment selected from the group consisting of degreasing, washing, phosphatizing and an abrasive blasting step.
 18. Method according to claim 15 or 16, wherein after having allowed the corrosion-inhibiting material to set the thickness of the layer of corrosion-inhibiting material is in the range of 10 to 30 μm.
 19. Method according to any one of claims 14 to 18, wherein the suspended particles of corrosion-inhibiting material further comprise a solid lubricant.
 20. Method according to any one of claims 14 to 19, wherein at least the threaded portion of the pipe component after having allowed the corrosion-inhibiting material to set, is at least partly covered with a layer of a lubricant.
 21. Method according to claim 19 or 20, wherein the lubricant is selected from the group consisting of molybdenum disulfide, tungsten disulfide, boron nitride, graphite, polytetrafluoroethylene (PTFE) and combinations thereof.
 22. An assembly of at least two oil well pipes, which are mutually connected by means of a sleeve-shaped coupling member, wherein at least one of the assembling parts, preferably including the coupling member, is an oil well component according to any one of the preceding claims 1-13. 